of the metal to pass through the whole range of colours. We find this phenomenon most beautifully exhibited in polished steel; but silver, copper, brass, lead, and tin, easily present similar appearances. A superficial oxydation is probably here taking place, as may be inferred from the effects of the operation when continued, especially in the more easily oxydizable metals.
512.
The same conclusion may be drawn from the fact that iron is more easily oxydizable by acid liquids when it is red hot, for in this case the two effects concur with each other. We observe, again, that steel, accordingly as it is hardened in different stages of its colorification, may exhibit a difference of elasticity: this is quite natural, for the various appearances of colour indicate various degrees of heat.42
513.
If we look beyond this superficial mantling, this pellicle of colour, we observe that as metals are oxydized throughout their masses, white or black appears with the first degree of heat, as may be seen in white lead, iron, and quicksilver.
514.
If we examine further, and look for the actual exhibition of colour, we find it most frequently on the plus side. The mantling, so often mentioned, of smooth metallic surfaces begins with yellow. Iron passes presently into yellow ochre, lead from white lead to massicot, quicksilver from æthiops to yellow turbith. The solutions of gold and platinum in acids are yellow.
515.
The exhibitions on the minus side are less frequent. Copper slightly oxydized appears blue. In the preparation of Prussian-blue, alkalis are